Intercalated compound

ABSTRACT

Embodiments of a metal oxide intercalated ink-jettable compound are disclosed.

BACKGROUND

Polyoxometalates may be utilized in electronic or display applications such as use in ionic conductors, electrochromic materials, and photochromic materials. It may be desirable to selectively deposit such materials to reduce manufacturing costs and improve product quality.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic view of one example embodiment of a process of manufacturing one example embodiment of an intercalated compound.

FIG. 2 is a side view of a inkjet printer depositing one example embodiment of a droplet of material including one embodiment of the intercalated compound.

FIG. 3 is a side view of a drop of an intercalated compound in solution.

FIG. 4 is a top view of an electronic device including a micro fabricated device including a deposited line of one example embodiment of the intercalated compound.

FIG. 5 is a top view of substrate including a coating of an intercalated compound in an inactivated state.

FIG. 6 is a top view of substrate including a coating of an intercalated compound in an activated state.

DETAILED DESCRIPTION OF THE DRAWINGS

FIG. 1 shows one example embodiment of a process of manufacturing one example embodiment of an intercalated compound 10. An intercalated compound may be defined as a compound having particles, ions, molecules, sub-compounds, elements, or the like, trapped or dispersed therein. Moreover, an intercalated metal oxide may be defined by layering at a molecular level whereas a metal oxide may be defined by a bulk particle in solution. Intercalated compound 10 is manufactured by first providing inorganic metal oxide compounds 12 which may be in the form of sheets 14 or layers positioned adjacent one another in a layered system 16 or stacked arrangement. The sheets 14 may be completely delaminated and may lack stacking coherence unless in the presence of guest ions or polymers. For ease of illustration, sheets 14 in the left hand portion of FIG. 1 are shown in a laminated arrangement, Metal oxide compounds 12 may be molybdenum oxide (MoO₃), tungsten oxide (WO₃), vanadium oxide (V₂O₅), or any other applicable metal oxide. In one example embodiment, three layers of molybdenum oxide are positioned adjacent one another in a three layered system 16. However, in other embodiments, other numbers of layers may be positioned adjacent one another. Layered system 16 may be in a solution 18, such as water. A preferred form of the oxide or the starting material is the modified oxide (i.e. metal ion intercalated oxide). Sodium ions may then be added to the solution 18 to form a sodium intercalated molybdenum intercalated layered system 20, as shown by Equation 1 below.

Na₂S₂O₄+MoO₃ +zH₂O→[Na⁺(H₂O)_(n)]_(x)[MoO₃ ^(x−)]+Na⁺+2SO²⁻+(z−n)H₂O  Equation 1

As shown in FIG. 1, sodium intercalated molybdenum oxide system 20, may include sheets of metal oxide 22, which may be referred to as host layers 22, and may have a negative charge, as indicated by the minus signs in FIG. 1. The MoO₃ sheets in the Na_(x)MoO₃ systems are negatively charged. The Na+ in the interlayer balances the charge on the MoO₃ sheets. Layers 24 of a cation, indicated by an “X” in FIG. 1, which in the example embodiment is sodium, may be intercalated between the host layers 22, and may have a positive charge as indicated by the plus sign next to “X”. This intercalated layered system 20 may be in a solution 26 of water, low molecular weight alcohols (ethanol, propanol, or 1,5-pentanediol) or polar aprotic solvents (2-pyrrolidone, methyl formamide, or dimethyl sulfoxide), or a combination thereof. Layered system 20 may also be referred to as stacks of negatively charged metal oxide sheets 22 with a layer 24 of a cation “X” positioned within the interlayer galleries 28. Cation “X” may be H, Li, Na, K, Rb, Cs, Tl, Au, Ag, NH₄ ⁺, or other organic cations.

The stacked layer arrangement of intercalated system 20, shown in the middle section of FIG. 1, is shown arranged in a neat stack for ease of illustration. In a preferred embodiment, sheets 22 and cations 24 may be free floating in solution, i.e., delaminated, and may not be orderly arranged in the stacked arrangement shown in the middle section of FIG. 1.

In the next step of manufacturing one example embodiment of an intercalated compound 10, an ion exchange of the first cation “X” with a second cation “Z” may be performed, as shown in Equation 2 below.

[Na⁺(H₂O)_(n)]_(x)[MoO₃ ^(x−)]+xLi⁺→[Li⁺(H₂O)_(n)]_(x)[MoO₃ ^(x−)]  Equation 2:

This step may result in layers 30 of negatively charged metal oxide sheets with a layer 40 of the second cation “Z” positioned in the interlayer galleries 42 of intercalated compound 10. Layer 40 may also referred to as a guest layer 40.

The product of Equation 2 may be collected and dried in air to yield a intercalated compound 10 having a deep blue color. If potassium is used as the second cation “Z”, the resulting intercalated compound 10 may have a light blue color. In example embodiments, the following colors may be produced: K×MoO₃, where x can be between 0 and 1 and produces a color in a range of blue bronze to red bronze, depending on the level of potassium intercalation, H_(x)MoO₃ having a blue bronze color, HxMoO₃ having a red bronze color, MoO₃(4,4′-bpy)_(0.5) having a yellow color, and H_(0.5)MoO₃(4,4′-bpy)_(0.5) having a black color. In another embodiment, compound 10 may be a MoO₃-citric acid stacked layer compound having multicolor photochromic properties.

In the next step of manufacturing one example embodiment of an intercalated compound 10, formation of a colloidal dispersion, i.e., exfoliation and suspension, may be performed, as shown in Equation 3 below.

[Li⁺(H₂O)_(n)]_(x)[MoO₃ ^(x−)]+H₂O (sonicated)→colloidal dispersion  Equation 3

The sonification of the reaction of Equation 3, in one example embodiment, may take place for approximately twenty minutes. In Equation 3, other polar solvents may be used in place of water.

As shown in FIG. 1, Equation 3 may be represented by the second reaction arrow in FIG. 1. After the reaction of Equation 3, and prior to the final formation of intercalated compound 10 as shown in FIG. 1, an organic polymer or an organic dye may be added to the solution 44 including colloidal dispersion 46 such that the organic material “O” may also be intercalated into interlayer galleries 42, along with second cation “Z”. In the embodiment shown, the first cation “X” is sodium and the second cation “Z” is lithium. However, other cations or mixtures thereof may be used for either of the first or second cations, such as hydrogen (H), lithium (Li), sodium (Na), potassium (K), rubidium (Rb), cesium (Cs), thallium (Tl), tin (Sn), chromium (Cr), manganese (Mn), copper (Cu), silver (Ag), gold (Au), or the like. The organic polymer or organic dye utilized may be one or more of polyvinyl alcohol (PVA), polyethylene glycol (PEG), polyethylene oxide (PEO), polyethylene imine (PEI), polyaniline (PANI), polypyrrole (PPY), polythiophene (PTh), polyvinyl acetate (PVOH), substituted analogs or copolymers, amines, pyridines, anilines, alkyl ammoniums, bipyridines, triazoles and a dye.

The amount of the second cation “Z” and the amount of the organic material “O” contained within interlayer 40 may depend on the amount of the individual reactants used. In some embodiments, second cation “Z” may not completely replace first cation “X” so that the first cation “X”, the second cation “Z”, and one or more of an organic material “O” may all be present in interlayer 40 of intercalated compound 10.

The amount of each material in intercalated compound 10 may be chosen as desired to produce an intercalated compound 10 having desired properties, as will be described below. In one example embodiment, the components of colloidal dispersion 46 may include DEG (2 wt %), 2-P (7%), IPA (4%), Surfynol 465 (0.1%), water (81.9%), and Li_(x)MoO₃ (2%).

In another example embodiment of the ink formulation process of intercalated compound 10, the following process was followed. Step one, 0.45 grams of PEG 600 was dissolved in 7 ml of water. This was stirred with a magnetic stirrer to ensure full dissolution. Step two, 0.6 g K_(x)MoO₃ was suspended in 7 ml of water. This was stirred magnetically to ensure full dispersion. Step three, the solution of step 2 was slowly added to the solution of step 1 while stirring. Step four, 1.5 g of DEG, 1.8 g pf 2-P, 0.9 g of IPA, and 0.06 g Surfynol 465 were blended in a beaker of 16 ml of water and mixed thoroughly. Step five, the solution of step four was added to the dispersion of step 3. Step six, the solution of step five was sonicated for five minutes using a power setting of not more than 5 to reduce overheating. Step seven, 12 ml of the solution of step six, which contained intercalated compound 10, was then placed in an inkjet print cartridge and printing was conducted.

The physical characteristics of the ink-jettable intercalated compounds 10 made by the above process are shown in Table 1 below:

Particle Size (nanotrac) Compound pH cond St Viscosity Mean Value (nm) Li_(x)MoO₃ 2.53 1.94 33.6 1.92 124.6 Na_(x)MoO₃ 4.13 510 37.1 1.11 90.8 K_(x)MoO₃ 2.82 1727 36.3 1.17 312.4

FIGS. 2 and 3 are a side view of a inkjet printhead 50 depositing one example embodiment of a droplet 52 of material including intercalated compound 10, and a side view of a droplet 52 including intercalated compound 10. Intercalated compound 10, in solution 44, may have a compound size of less than 200 nm, and approximately 150 nm, which is smaller than a size, such as less than 1 μm, of the individual ones of nozzles 54 of an inkjet printhead 50. The nozzle size may depend on the printer platform used, and may be much larger than 1 micron.

Due to the small size of intercalated compound 10, and its ability to be ejected through the small orifices of nozzles 54 of inkjet printhead 50, intercalated compound 10 may be selectively deposited on a substrate 56 in a precise, predetermined pattern. Accordingly, intercalated compound 10 may be deposited to form a pattern, such a discrete micro fabricated, microelectronic component 58 (see FIG. 4) on substrate 56, without the use of multiple masking, deposition and etching steps. Accordingly, ink-jettable intercalated compound 10 may allow the production of microelectronic components 58 in a cost effective manner, with high quality and large throughput.

Intercalated compound 10 may have very good stability for at least two reasons: the organic polymer materials may inhibit agglomeration, and the negative charge of sheets 22 may attract the positive intercalated compound within the interlayer galleries and cause the destabilization of the dispersion. In a preferred embodiment, this attraction of the negative charge on sheets 22 and the positive intercalated compound will occur during printing on a suitable substrate, not when the ink is in the cartridge. For example, in one experimental embodiment, an inkjet pen was filled with a intercalated compound 10 of MoO₃-bronze and printed. The ink pen was then stored at room temperature for four months, after which the pen was seen to continue to produce high quality printed product.

Still referring to FIGS. 2 and 3, ink-jettable intercalated compound 10 may also include visible metallic luster properties. In particular, intercalated compound 10 may provide a stable ink suspension, which may include a color dye, that may be deposited by an ink jet structure to provide a printed ink having a metallic luster, also referred to as a metallic shine. Due to the small size of intercalated compound 10, and due to the stability of the intercalated compound 10, the metallic luster ink may be deposited by ink jet methods, such that the metallic luster ink may be deposited in digital imaging applications and/or micro electronic applications. The printed ink of intercalated compound 10 has a metallic luster characteristic of a true metal nanoparticle, i.e., metal oxide layering with metallic cation guests at the nano-level, as opposed to a large metallized plastic particles that may not be amenable to ink jet deposition methods. The metallic cation guests that have been shown or believed to give intercalated compound 10 its metallic luster include, but are not limited to, Au, Ag, Li, Na, H+ and K.

FIG. 4 is a top view of an electronic device 60 formed on a substrate 56. Electronic device 60 may include micro fabricated component 58 including a deposited amount of one example embodiment of the intercalated compound 10. Device 60 may have application in molecular electronics, energy storage, optics, displays, catalysis, photochromic devices, and electrochromic devices. MoO₃ and the WO₃ composite materials may be semiconductors, such that intercalated compound 10 may be tailored with the addition of conductive and/or non-conductive organic materials. In some example embodiments, micro fabricated component 58 may be an electrically conductive trace, an ionically conductive trace, a solid state electrolyte having ionic transport properties, or a switchable light window, either photo or electro based. The organic portion of intercalated compound 10 may be a conductor (such as polyaniline) or an insulator. In some applications, the organic material may be thermally removed if desired.

In several example embodiments, the electrical conductivity, as a function of thermal exposure, was measured. A two point test configuration was used to measure the conductance. For an intercalated compound 10 of Na_(x)MoO₃, with a probe spacing of 1 millimeters (mm), 2 mm, 3 mm, and 4 mm, respectively, the conductance was measured as 158 ohms, 186 ohms, 206 ohms, and 218 ohms, respectively. For an intercalated compound 10 of Li_(x)MoO₃, with a probe spacing of 1 mm, 2 mm, 3 mm, and 4 mm, respectively, the conductance was measured as 526 ohms, 670 ohms, 832 ohms, and 923 ohms, respectively. For an intercalated compound 10 of K×MoO₃, with a probe spacing of 4 mm, the conductance was measured as 10,100 ohms. The conductivities presented here are for a particular example embodiment and are not optimized.

FIG. 5 is a top view of a 62 substrate including a coating 64 of an intercalated compound 10 in an inactivated state. In this inactivated state, intercalated compound 10 may be clear or colorless.

FIG. 6 is a top view of substrate 62 including a coating 64 of an intercalated compound 10 in an activated state. In this activated state, intercalated compound 10 may be colored. Accordingly, intercalated compound 10 may be used in “smart windows” applications, such as electrochromics and/or photochromics. Coating 64 may be activated by application of an applied current by the use of leads (not shown) or by application of light, such as sunlight, for example. In one example embodiment, movement from the inactivated state to the activated state, by electrochromic application of an applied current, may be shown by the following Equation 4 below:

MO₃*nH₂O+mX+xe⁻(transparent)

X_(m)MO₃*nH₂O (colored), where M=Mo or W  Equation 4

In another example embodiment, movement from the inactivated state to the activated state, by photochromic light application, may be shown by the following Equation 5 below:

MO₃*nH₂O+mX+hv (transparent)

X_(m)MO₃*nH₂O (colored), where M=Mo or W  Equation 5:

In another example use of intercalated compound 10, the compound may be a MoO₃-PANI stacked layer compound having sensor properties adapted to sense toxic gases and volatile organic compounds. PANI is an electronically conducting polymer which has a simple doping/undoping chemistry based on acid/base reactions. The basic form is relatively non-conducting whereas the acidic form is conductive. The sensing principle is based on the fact that when the blue non-conducting emeraldine base PANI comes into contact with acidic gas such as HCl or H₂S, it rapidly becomes doped to form the green conducting emeraldine salt (acidic form). This change results in a dramatic decrease in the resistance—a principle used in gas sensors.

According, there is disclosed, an ink-jettable intercalated compound 10 that may be deposited using inkjet techniques. Such selective application of intercalated compound 10 may reduce material waste, reduce tooling and operational costs, and may allow a significant improvement in design flexibility. The example intercalated compounds 10 disclosed are environmentally stable, even in the conducting state, and may be fabricated using various methodologies, unlike traditional 1-D and 3-D materials. Moreover, device fabrication by the use of inkjet deposition is amenable to large-scale manufacturing processes.

Other variations and modifications of the concepts described herein may be utilized and fall within the scope of the claims below. 

1. An intercalated, ink-jettable compound, comprising: a stacked layer compound including alternating layers of a first material and a second material, said stacked layer compound having a size adapted for deposit through nozzles of an inkjet printing device; said first material comprising an inorganic metal oxide; and said second material comprising at least one of an organic polymer and an organic dye.
 2. The compound of claim 1 wherein said first material is chosen from one of molybdenum oxide, vanadium oxide, and tungsten oxide.
 3. The compound of claim 1 wherein said second material is chosen from one of polyvinyl alcohol (PVA), polyethylene glycol (PEG), polyethylene oxide (PEO), polyethylene imine (PEI), polyaniline (PANI), polypyrrole (PPY), polythiophene (PTh), polyvinyl acetate (PVOH), substituted analogs or copolymers thereof, amines, pyridines, anilines, alkyl ammoniums, bipyridines, triazoles and a dye.
 4. The compound of claim 1 wherein said stacked layer compound includes at least two layers of said first material and at least one layer of said second material.
 5. The compound of claim 1 wherein said stacked layer compound has a size of at most 200 nm
 6. The compound of claim 1 wherein said compound is electrically conductive.
 7. The compound of claim 1 wherein said compound includes electrochromic properties and is activated between first and second states, wherein in the first state said compound defines a color and in the second state said compound is colorless.
 8. The compound of claim 1 wherein at least a portion of said second material comprises a cation.
 9. The compound of claim 1 wherein said compound is in solution in a form chosen from one of a polymeric/organic intercalated colloid, a polymer stabilized particle, and a polymeric suspension of exfoliated sheets.
 10. The compound of claim 1 wherein said compound comprises a colorant chosen from one of K_(0.33)MoO₃ having a red bronze color, K_(0.30)MoO₃ having a blue bronze color, H_(x)MoO₃ having a blue bronze color, H_(x)MoO₃ having a red bronze color, MoO₃(4,4′-bpy)_(0.5) having a yellow color, and H_(0.5)MoO₃(4,4′-bpy)_(0.5) having a black color.
 11. The compound of claim 1 wherein said compound comprises a MoO₃-PANI stacked layer compound having sensor properties adapted to sense acidic and basic gases and volatile organic compounds.
 12. The compound of claim 1 wherein said compound comprises a MoO₃-citric acid stacked layer compound having multicolor photochromic properties.
 13. The compound of claim 1 wherein said compound is a solid electrolyte and includes ionic transport properties.
 14. The compound of claim 1 wherein said compound is chosen from one of Na_(x)MoO₃ having a resistance of less than 200 ohms at a probe spacing of 1 mm, Li_(x)MoO₃ having a resistance of less than 800 ohms at a probe spacing of 1 mm, and K_(x)MoO₃ having resistance of greater than 10,000 ohms at a probe spacing of 4 mm.
 15. The compound of claim 1 wherein said compound has visible metallic luster properties.
 16. An ink-jettable, polyoxometalate compound, comprising: alternating layers of a first material and a second material; said first material comprising an oxomatelate; said second material comprising a mixture of an organic material and a cation; and wherein said alternating layers define a compound size adapted for deposit though an inkjet printing nozzle.
 17. The compound of claim 16 wherein said first material is chosen from one of MoO₃,V₂O₅, and WO₃, wherein said organic material of said second material is chosen from one of polyvinyl alcohol (PVA), polyethylene glycol (PEG), polyethylene oxide (PEO), polyethylene imine (PEI), polyaniline (PANI), polyvinyl acetate (PVOH), amines, pyridines, anilines, alkyl ammoniums, bipyridines, triazoles and a dye, and wherein said cation of said second material is chosen from one of H, Li, Na, K, Rb, Cs, Tl, Ag, Au, NH₄ ⁺, and organic cations.
 18. A method of manufacturing an ink-jettable intercalated organic/inorganic metal oxide compound, comprising: providing an inorganic metal oxide in solution; adding a cation to said solution to form an intercalated structure including alternating layers of said inorganic metal oxide and said cation; and adding an organic material to said solution wherein said organic material replaces at least a portion of said cation in said intercalated structure to from an intercalated organic/inorganic layered structure including alternating layers of said inorganic metal oxide and a mixture of said cation and said organic material.
 19. The method of claim 18 wherein said cation is chosen from one of H, Li, Na, K, Rb, Cs, Tl, Ag, Au, NH₄ ⁺, and organic cations.
 20. The method of claim 18 wherein said inorganic metal oxide is chosen from one of MoO₃ and WoO₃ and wherein said solution is water.
 21. The method of claim 18 further comprising adding a second cation to said solution wherein said second cation exchanges with said cation to form an intercalated structure including alternating layers of said inorganic metal oxide and a mixture of said second cation and said organic material.
 22. The method of claim 18, prior to said adding an organic material, further comprising, sonicating said intercalated structure including alternating layers of said inorganic metal oxide and said cation, to form a colloidal dispersion.
 23. A method of depositing an intercalated metal oxide, comprising: placing a printable amount of a solution in an inkjet printer having a plurality of inkjet nozzles therein, said solution including an intercalated metal oxide; and printing said solution including said intercalated metal oxide through individual ones of said plurality of inkjet nozzles of said inkjet printer.
 24. The method of claim 23 wherein said solution comprises a stacked layer compound including alternating layers of an inorganic metal oxide and at least one of an organic polymer, an organic dye and a cation, wherein said stacked layer compound has a size adapted for deposit through individual ones of said plurality of nozzles.
 25. The method of claim 23 wherein said solution is printed through said individual ones of said plurality of inkjet nozzles to form a coating on a substrate, wherein said coating is chosen from one of an electrochromic device and a photochromic device.
 26. The method of claim 23 wherein said solution is printed through said individual ones of said plurality of inkjet nozzles to form a micro fabricated electronic device on a substrate.
 27. The method of claim 23 wherein said solution includes metallic luster properties.
 28. A method of generating a colored image, comprising: providing an inorganic metal oxide in solution; adding a cation to said solution to form an intercalated structure including alternating layers of said inorganic metal oxide and said cation; and adding an organic material to said solution wherein said organic material replaces at least a portion of said cation in said intercalated structure to form an intercalated organic/inorganic layered structure including alternating layers of said inorganic metal oxide and a mixture of said cation and said organic material. 